Cream Time (s):7-9
End of Rise Time (s):50-60
Free Rise Foam Density(g/cm3):0.13-0.16
Mold Temperature (℃):45-55
Hardness (Shore C ):35-45

Kontakta nu

Produktbeskrivning

Produktegenskaper

Emballage og levering

Produktbeskrivning

Produktegenskaper

Modell nr: A-2001/B-8580

Märke: Xuchuan kemikalie

Härstamning: Kina

Typer Av: Syntetiskt harts och plast

Application: Insole and low density mid-sole

Characteristic: Good handle, low density and good dimension stability, high elasticity

Appearance: Liquid

Brand: Xuchuan

Code: A-2001/B-8580

Emballage og levering

Sælgende enheder	:	Kilogram
Pakketype	:	20 & 225 kg/trumma
Billedeksempel	:

Produktbeskrivning

Polyolisocyanat för mitten av solen

Gjutning av polyuretanharts för skon i mitten av solstolen

Skosula pu kemikalie

Skosula polyuretanhartser

Produktdetalj

Application	shoes insole
A/B Materials Temperatures (℃)	40~45/38~42
A+C/B Mix ratio (By weight)	100/74~76
Cream Time (s)	7~9
End of Rise Time (s)	50~60
Free Rise Foam Density(g/cm3)	0.13~0.16
Mold Temperature (℃)	45~55
Molded Density (g/cm3)	0.30~0.40
Hardness (Shore C )	35~45
Tensile strength(MPa)	Tensile strength(MPa)

Characteristic: Good handle, low density and good dimension stability, high elasticity
Application: Insole and low density mid-sole
Typical properties of PU matrix
Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm^-3/40℃)	Package(kg)	/
A-2001	Liquid	1000~1400	1.01~1.02	18
B-8580	Yellowish transparent liquid or waxy	600~1000	1.08~1.2	20
Materials preheat
A-2001: preheated at 50~60℃ for 8~10 hours.
B-8580: preheated at 50~60℃ for 8~12 hours.
Typical processing parameters & Reaction parameter
Items	A/B Materials Temperatures (℃)	A+C/B Mix ratio (By weight)	Cream Time (s)	End of Rise Time (s)	Free Rise Foam Density(g/cm³)	Mold Temperature (℃)	Demold Time(min)

Parameter	40~45/38~42	100/74~76	7~9	50~60	0.13~0.16	45~55	4~5
The adding content of C-2 should be 300g±20g/18kg.
The adding content of water should be 0~90g/18kg according to the reality.
Physical properties
Items	Molded Density (g/cm³)	Hardness (Shore C )	Tensile strength(MPa)	Elongation (%)	Tear Strength (kN/m)	/

Physical properties	0.30~0.40	35~45	4.0~6.0	300~380	18~26
Demold time may be prolonged with the increase of sole thickness
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Företagsöversikt

company company

Xuchuan Chemical som grundades 2007, företaget registrerat kapital är 500 miljoner RMB. Huvudprodukterna är alla områden polyesterpolyol, polyuretanharts för skor, vattenbaserade och lösningsmedelsfria polyuretanhartser för konstgjorda läder, polyuretanbindningslim och polyuretan varmmältlim.

Nu har Xuchuan fyra moderna produktionsbaser, produktionskapacitet nådde 630 000 ton per år, produkter exporterade till 32 länder och regioner i världen.

Verkstad