Flytande polyuretanhartsskum för att göra innersula
Få Senaste PrisBetalning Typ: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Beställ: | 1000 Kilogram |
Transportfordon: | Ocean,Land,Air |
Hamn: | Shanghai |
Betalning Typ: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Beställ: | 1000 Kilogram |
Transportfordon: | Ocean,Land,Air |
Hamn: | Shanghai |
Modell nr: XC-9080W,XC-6088
Märke: Xuchuan kemikalie
Härstamning: Kina
Typer Av: Syntetiskt harts och plast
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Appearance: Liquid
Application: shoe sole
Keywords: liquid polyurethane resin,insole material memory foam,insole foam
Polyolisocyanat för mitten av solen
Application | shoe sole |
Keywords | liquid polyurethane resin,insole material memory foam,insole foam |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical som grundades 2007, företaget registrerat kapital är 500 miljoner RMB. Huvudprodukterna är alla områden polyesterpolyol, polyuretanharts för skor, vattenbaserade och lösningsmedelsfria polyuretanhartser för konstgjorda läder, polyuretanbindningslim och polyuretan varmmältlim.
Nu har Xuchuan fyra moderna produktionsbaser, produktionskapacitet nådde 630 000 ton per år, produkter exporterade till 32 länder och regioner i världen.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.