Cream Time (s):8-10
End of Rise Time (s):60-70
Mold Temperature(℃):45-55
Demold Time(min)

Kontakta nu

Produktbeskrivning

Produktegenskaper

Emballage og levering

Produktbeskrivning

Produktegenskaper

Modell nr: A-3070,B-8280

Märke: Xuchuan kemikalie

Härstamning: Kina

Typer Av: Syntetiskt harts och plast

Characteristic: Good handle, smooth surface

Appearance: Liquid

Name Of Products: A-3070,B-8280

Brand: Xuchuan

Application: Industrial tyre wheel

Product Name: Polyurethane

Emballage og levering

Sælgende enheder	:	Kilogram
Pakketype	:	220 kg/trumma
Billedeksempel	:

Produktbeskrivning

PRODUKTBESKRIVNING

Pu hjulkemikalier

PU -harts flytande polyuretanvattentätning alifatik för skumdäck

Hjulpolyuretangjutningsharts

Anpassade hjul PU -material

Produktdetalj

Application	Industrial tyre wheel
Product name	Polyurethane
A/B Materials Temperatures(℃)	40~45/38~42
A+C/B Mix ratio (By weight)	100/101~103
Cream Time (s)	8~10
End of Rise Time (s)	60~70
Free Rise Foam Density(g/cm3)	0.24~0.26
Mold Temperature(℃)	45~55
Demold Time(min)	5~7

Characteristic: Good handle, smooth surface
Application: Tire
Typical properties of PU matrix
Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm^-3/40℃)	Package(kg)	/
A-3070	Liquid	1000~1400	1.01~1.02	18
B-8280	Yellowish transparent liquid or waxy	800~1200	1.08~1.2	20
Materials preheat
A-3070: preheated at 50~60℃ for 6~8 hours.
B-8280: preheated at 50~60℃ for 10~12 hours.
Typical processing parameters & Reaction parameter
Items	A/B Materials Temperatures(℃)	A+C/B Mix ratio (By weight)	Cream Time (s)	End of Rise Time (s)	Free Rise Foam Density(g/cm³)	Mold Temperature(℃)	Demold Time(min)

Parameter	40~45/38~42	100/101~103	8~10	60~70	0.24~0.26	45~55	5~7
The adding content of C-2 should be 250g±10g/18kg
The adding content of water should be 0~90g/18kg according to the reality
The adding content of hardener should be 0~600g/18kg according to the reality
Physical properties
Items	Molded Density (g/cm3)	Hardness (Shore A )	Tensile strength (MPa)	Elongation (%)	Tear Strength (kN/m)

Physical properties	0.50~0.70	55~68	7.5~9.0	340~450	24~33
Demold time may be prolonged with the increase of sole thickness.
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Data som anges ovan är bara för referens. Detaljdata utsätts för praktisk produktion. Om andra förfrågningar om fysiska egenskaper, vänligen kontakta oss.

Företagsöversikt

company company

Xuchuan Chemical som grundades 2007, företaget registrerat kapital är 500 miljoner RMB. Huvudprodukterna är alla områden polyesterpolyol, polyuretanharts för skor, vattenbaserade och lösningsmedelsfria polyuretanhartser för konstgjorda läder, polyuretanbindningslim och polyuretan varmmältlim.

Nu har Xuchuan fyra moderna produktionsbaser, produktionskapacitet nådde 630 000 ton per år, produkter exporterade till 32 länder och regioner i världen.

Verkstad