Polyuretanhartsmaterial för sandaler
Få Senaste PrisBetalning Typ: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Beställ: | 1000 Kilogram |
Transportfordon: | Ocean |
Hamn: | Shanghai |
Betalning Typ: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Beställ: | 1000 Kilogram |
Transportfordon: | Ocean |
Hamn: | Shanghai |
Modell nr: A-2001/B-8580
Märke: Xuchuan
Härstamning: Kina
Typer Av: Syntetiskt harts och plast
Application: Insole and low density mid-sole
Characteristic: Good handle, low density and good dimension stability, high elasticity
Appearance: Liquid
Cream Time (s): 7-9
PRODUKTBESKRIVNING
Skosula pu kemikalie
Application | shoes insole |
A/B Materials Temperatures (℃) | 40~45/38~42 |
A+C/B Mix ratio (By weight) | 100/74~76 |
Cream Time (s) | 7~9 |
End of Rise Time (s) | 50~60 |
Free Rise Foam Density(g/cm3) | 0.13~0.16 |
Mold Temperature (℃) | 45~55 |
Molded Density (g/cm3) | 0.30~0.40 |
Hardness (Shore C ) | 35~45 |
Tensile strength(MPa) | Tensile strength(MPa) |
Characteristic: Good handle, low density and good dimension stability, high elasticity |
|||||||
Application: Insole and low density mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
||
A-2001 |
Liquid |
1000~1400 |
1.01~1.02 |
18 |
|||
B-8580 |
Yellowish transparent liquid or waxy |
600~1000 |
1.08~1.2 |
20 |
|||
Materials preheat |
|||||||
A-2001: preheated at 50~60℃ for 8~10 hours. |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours. |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/74~76 |
7~9 |
50~60 |
0.13~0.16 |
45~55 |
4~5 |
The adding content of C-2 should be 300g±20g/18kg. |
|||||||
The adding content of water should be 0~90g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength(MPa) |
Elongation (%) |
Tear Strength |
/ |
|
Physical properties |
0.30~0.40 |
35~45 |
4.0~6.0 |
300~380 |
18~26 |
||
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Polyuretan råvaror
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.