Modell nr: A-2260/B-8580
Märke: Xuchuan kemikalie
Härstamning: Kina
Typer Av: Syntetiskt harts och plast
Application: Outsole and mid-sole
Characteristic: Good handle, low density and good dimension stability
Appearance: Liquid
PRODUKTBESKRIVNING
Polyuretan råvaror
Skosula pu kemikalie
Application | shoe sole |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 40~50 |
Free Rise Foam Density(g/cm3) | 0.15~0.25 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 2.5~3.5 |
Molded Density (g/cm3) | 0.30~0.45 |
Hardness(Shore A ) | 43~58 |
Tensile strength(MPa) | 1.5~4.5 |
Elongation(%) | 250~400 |
Polyuretan för skorsula:
Densitet: 300 ~ 500 kg/m3.
Hårdhet: 45 ~ 75shore A.
Bra kompatibilitet med pigment.
Breskt förhållande.
Characteristic: Good handle, low density and good dimension stability |
|||||||
Application: Outsole and mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-2260 |
Cream white liquid |
800~1200 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-8580 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-2260: preheated at 50~60℃ for 8~10 hours |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/96~98 |
6~8 |
40~50 |
0.15~0.25 |
45~55 |
2.5~3.5 |
The adding content of C-2 should be 270g±20g/18kg |
|||||||
The adding content of water should be 0~100g/18kg according to the reality |
|||||||
The adding content of hardener should be changed according to the reality |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness (Shore A ) |
Tensile strength (MPa) |
Elongation (%) |
Tear Strength (kN/m) |
Ross Flexing (room temperature) ( 40,000 times) |
/ |
/ |
|||||||
/ |
|||||||
Physical properties |
0.30~0.45 |
43~58 |
1.5~4.5 |
250~400 |
10~26 |
No crack |
/ |
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical som grundades 2007, företaget registrerat kapital är 500 miljoner RMB. Huvudprodukterna är alla områden polyesterpolyol, polyuretanharts för skor, vattenbaserade och lösningsmedelsfria polyuretanhartser för konstgjorda läder, polyuretanbindningslim och polyuretan varmmältlim.
Nu har Xuchuan fyra moderna produktionsbaser, produktionskapacitet nådde 630 000 ton per år, produkter exporterade till 32 länder och regioner i världen.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.