Cream Time (s):6-8
End of Rise Time (s)：30~40
Mold Temperature(℃):45~55
Molded Density (g/cm3)：0.35~0.60

Kontakta nu

Produktbeskrivning

Produktegenskaper

Emballage og levering

Produktbeskrivning

Produktegenskaper

Modell nr: A-9088W,B-6088

Märke: Xuchuan kemikalie

Härstamning: Kina

Typer Av: Syntetiskt harts och plast

Name Of Product: A-9088W/B-6088

Keywords: pu molding,polyurethane resin for casting,material straps for sandals

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line

Appearance: liquid

Application: shoe sole

Emballage og levering

Sælgende enheder	:	Kilogram
Pakketype	:	220 kg/trumma
Billedeksempel	:

Produktbeskrivning

PRODUKTBESKRIVNING

Polyuretan råvaror

PU -gjutning av polyuretanhartsmaterial för gjutband sandaler

Skosula pu kemikalie

Produktdetalj

Application	shoe sole
Keywords	pu molding,polyurethane resin for casting,material straps for sandals
A/B Materials Temperatures(℃)	A/B Materials Temperatures(℃)
A+C/B Mix ratio (By weight)	100/100~102
Cream Time (s)	6~8
End of Rise Time (s)	30~40
Free Rise Foam Density(g/cm3)	0.21~0.26
Mold Temperature(℃)	45~55
Demold Time(min)	Demold Time(min)
Molded Density (g/cm3)	0.35~0.60

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Application: Outsole, slippers, wedge shoes
Typical properties of PU matrix
Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm^-3/40℃)	Package(kg)	/	/	/
A-9080W	Cream,White,liquid	1000~1300	1.01~1.02	18	/	/	/
B-6088	Yellowish transparent liquid or waxy	600~800	1.08~1.2	20	/	/	/
Materials preheat
A-9080W: preheated at 50~60℃ for 6~8 hours.
B-6088: preheated at 50~60℃ for 6~8 hours.
Typical processing parameters & Reaction parameter.
Items	A/B Materials Temperatures(℃)	A+C/B Mix ratio (By weight)	Cream Time (s)	End of Rise Time (s)	Free Rise Foam Density(g/cm³)	Mold Temperature(℃)	Demold Time(min)

Parameter	40~45/38~42	100/100~102	6~8	30~40	0.21~0.26	45~55	5~7
The adding content of C-2 should be 210g±10g/18kg.
The adding content of water should be 0~80g/18kg according to the reality.
The adding content of hardener should be 0~1200g/18kg according to the reality.
Physical properties
Items	Molded Density (g/cm³)	Hardness (Shore A )	Tensile strength (MPa)	Elongation (%)	Tear Strength (kN/m)	Williams abrasion (cc/php)	/
Physical properties	0.35~0.60	60~88	4~7	200~300	11~20	130~200	/
Demold time may be prolonged with the increase of sole thickness.
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Polyolisocyanat för mitten av solen

Företagsöversikt

company company

Xuchuan Chemical som grundades 2007, företaget registrerat kapital är 500 miljoner RMB. Huvudprodukterna är alla områden polyesterpolyol, polyuretanharts för skor, vattenbaserade och lösningsmedelsfria polyuretanhartser för konstgjorda läder, polyuretanbindningslim och polyuretan varmmältlim.

Nu har Xuchuan fyra moderna produktionsbaser, produktionskapacitet nådde 630 000 ton per år, produkter exporterade till 32 länder och regioner i världen.

Verkstad